Thermoplastic "Leader"

Thermoplastic Lider white glass bead container 1000 kg
Thermoplastic Lider white glass bead container up to 1000 kg

56,00 rbl./kg
Of 62.00 RUB/kg

Order

Thermoplastic "Leader" is white with 20% glass bead container, 1000 kg
Thermoplastic "Leader" is white with 20% glass bead container, up to 1000 kg

58,14 RUB/kg
Of 71.00 RUB/kg

Order

Thermoplastic Lider yellow, without glass bead container, 1000 kg
Thermoplastic Lider yellow, without glass bead container, up to 1000 kg

59,16 rbl./kg
76,50 RUB/kg

Order

Thermoplastic Lider yellow, with 20% glass bead container, 1000 kg
Thermoplastic Lider yellow, with 20% glass bead container, up to 1000 kg

63,85 RUB/kg
80,50 RUB/kg

Order

Thermoplastic "Leader" of the orange, without glass bead container, 1000 kg
Thermoplastic "Leader" of the orange, without glass bead container, up to 1000 kg

65,00 RUB/kg
Of 82.00 RUB./kg

Order

  • The velocity of the composition, g/s, not less than 3,8
  • Curing time at 20°C/ min, not more than 14
  • Softening temperature, °C, not less 96,6
  • Brightness, %, not less than 70
  • The temperature of the coating, °C, not below +10
  • Consumption (at layer thickness of 4 mm.) kg/m2 8

Purpose:

Thermoplastic marking stamps city "Leader" of the optimal ratio price-quality. Are made on the basis of petroleum resin C5 and supplied to the customer in bulkor type of wet sand mixture of white colour, used on roads of different categories. Made with beads or without them.

Application:

Thermoplastic marking stamps city "Leader" processing temperature of the material 150+/- 10°C. To provide retroreflection at night in thermoplastic introduces glass microspheres. Placed in polyethylene bags 15 kg bags and shipped on pallets of 1 ton. Thermoplastic is applied to dry, cleaned from dirt road surface. The thickness of the coating of thermoplastic on the road surface is 2-4 mm. At operating temperature before starting work molten thermoplastic must be aged for at least 40 minutes with constant stirring. The ambient temperature during application should not be below 10°C, relative humidity not more than 85%. At a lower temperature is heated roadway. To ensure visibility of road markings in the dark it is necessary to apply the beads. Glass beads sprinkled on the surface of the thermoplastic material through nozzles mounted in marking machines, the rate of up to 400 g glass bead container at 1 m markings.

The application of thermoplastic on the road surface machine

Specifications

Thermoplastic "Leader" - thermoplastic road single-component mass used for horizontal marking of the carriageway of roads.

Thermoplastic is manufactured in two versions: without glass bead container, and beads to provide retro-reflective effect in the night time during the life of the marking. The contents of the glass bead container – 20%. Dusting with glass beads applied on top of thermoplastic material is carried out in order to obtain reflective effectt is based 250-350 g/m2.

The applied thermoplastic marking machine carriage or extruder type. To ensure the quality of marking should be further guided by the instructions of road marking machines and fallopian boiler.

The thickness of the coating of thermoplastic on the road surface is 2 - 4 mm. the Flow of thermoplastic material with a layer thickness of 4 mm - 8 kg/m2.

  Specifications Thermoplastic "Leader" Control method
1 Appearance Loose or wet sand type mixture of light gray color, containing lumps up to 10 mm., melts when heated visually
2 The velocity of the composition at the operating temperature (180±20)°C, g/s 3,8 p. 5.2.1 GOST 8420
3 Softening temperature, °C, not less 96,6 p. 5.3.1 GOST 11506
4 Luminance factor the colour white % min color yellow, no less 70 / 40 p. 5.4.2 GOST 896
5 Curing time at (20±2)°C and humidity (65±5)%, min, max 14 p. 5.5.2 GOST 19007
6 The content of glass microspheres, % 20  