Cold plastic "Start CP"
|Cold plastic Start KHP (white), kg||146 RUB/kg||Order|
|Cold plastic Start KHP (white) with glass beads, kg||148 RUB/kg||Order|
|Cold plastic Start KHP (yellow), kg||148 RUB/kg||Order|
|Cold plastic Start KHP (yellow) with glass beads, kg||150 RUB./kg||Order|
|Cold plastic Start CPS (green), kg||165 RUB/kg||Order|
|Cold plastic Start HP (red), kg||165 RUB/kg||Order|
|Cold plastic HP (blue) THAT 20.16.59-006-41982914-2017 kg||165 RUB/kg||Order|
- Viscosity by VZ-246 (nozzle diameter 4 mm) at 20±2°C, sec. at least 60
- Drying time at 20±2°C, not more than 20 min.
- Luminance factor,%, not less 80
- Adhesion (to glass), points, not more than 2
- The degree of milling on the device "Wedge", mkm, not more than 40
- Density, g/cm3, not less than 1.4
- The expense of paint with a layer thickness of 0.4 mm (wet), kg/m2, not more than 0.6
Cold plastic "Start CP" is an innovative material, Superior to all other known marking materials. Its characteristics cold plastic is not inferior to the thermoplastic material and its use does not require costly road equipment.
Two component cold plastic "Start CP" is for Naninclusion of horizontal road marking on asphalt road surfaces roads, Parking of vehicles, storage areas, pedestrian crossings (zebras), for the production of "noise lines". Applied with placemarkers or manually with a spatula. Two component cold plastic "Start CP" – is a viscous thixotropic liquid white eiropadomes with a characteristic odor, which is a dispersion of coarse and fine-grained fillers, pigments, processing additives in the mixture of esters of methacrylic/acrylic acid. A curing agent (polymerization initiator) is dibenzoylperoxide in phthalates – white powder.
The application of cold plastic manual slide
Cold plastic is designed for applying horizontal road marking on asphalt road surfaces roads, Parking of vehicles, storage areas, pedestrian crossings, in the production of noise lines.
Cold plastic for road marking "Start CP" is an innovative road-marking material which has a high wear resistance combined with excellent adhesion to the asphalt surface and the old road markings. Its characteristics cold plastic is not inferior to the thermoplastic.
Applied with placemarkers in hand with a spatula.
Basic colors: white, yellow, red.
- THAT 2241-002-66853081-2013
- complies with GOST R 52575-2006
|Specifications||Start HP||Control method|
|1||Appearance||A thick homogeneous liquid||p. 5.2|
|2||CoEefficient brightness cured of cold plastic, color white, classes, B6, B7, %, more than the color yellow, the classes B3, B4, %, more than the color orange, classes B2, B3 %, more||70 / 40 / 30||p. 5.4 896 GOST GOST R 52575 GOST R 52576|
|3||The density of the cured cold plastic class FG1, g/cm3, more class PP2, g/cm3 class FG3, g/cm3, less||2,1 / 1,9-2,1 / 1,9||p. 5.5 GOST 12801 GOST R 52575 GOST R 52576|
|4||The curing time of cold plastic at a temperature of (20±2) °C and humidity (65±5) % to the degree of drying 3, grade VT1, min.||10-20||p. 5.6 GOST 19007 52575 GOST R GOST R 52576|
|5||Vitality cured of cold plastic to static impact: -3 %-aqueous solution of sodium chloride at a temperature of (0±2) °C, hour, not less -saturated aqueous solution of sodium chloride at a temperature of (0±2) °C, hour, not less -water at a temperature of (20±2) °C, hour, not less than -10% aqueous alkali solution of sodium hydroxide at a temperature of (20±2) °C, hour, not less||72 / 72 / 72 / 72||p. 5.7 GOST 9.403 GOST R 52575 GOST R 52576|